Repair & rebuild all types of equipment!
Engineered to Repair Deeply Damaged Components.
Cures to a Metal Hard, Ceramic-Like Finish.
METALCLAD CeramAlloy CP+AC is a two component, 100% solids, polymer composite specifically formulated to provide effective repair and rebuilding characteristics on all types of fluid flow equipment.
METALCLAD CeramAlloy CP+AC is a paste when mixed, so it is easily applied. When cured, however, CP+AC becomes a metal-hard, ceramic-like compound.
METALCLAD CeramAlloy CP+AC is the best material to use when making repairs to areas deeply damaged by erosion/corrosion environments on all types of fluid flow components.
- Trowelable
- Requires No Heat
- Unlimited Shelf Life
- 100% Solids
- Safe & Simple To Use
Use for
Heat Exchanger Tube Sheets & Water Boxes, Pumps, Valves & Pipework, Housings & Tanks, Cooling Towers, etc.
Technical Data
- Volume capacity per kg.
- 36 in3 / 592 cc
- Mixed density
- 0.061 lbs per in3 / 1.69 gm per cc
- Coverage rate per kg. @ 0.25 in / 6mm
- 144 in2 / 0.092 m2
- Shelf life
- Indefinite
- Volume Solids
- 100%
| Mixing ratio | Base | Activator |
|---|---|---|
| By Volume | 5 | 2 |
| By Weight | 3.6 | 1 |
Working Life and Cure Times
| Ambient Temperature | Working Life | Machining Light Load | Full Mechanical | Chemical Immersion | |
|---|---|---|---|---|---|
| 41°F | 5°C | 4 hrs. | 48 hrs. | 96 hrs. | 8 days |
| 59°F | 15°C | 2 hrs | 24 hrs. | 48 hrs. | 5 days |
| 77°F | 25°C | 1 hr | 12 hrs. | 24 hrs. | 3 days |
| 86°F | 30°C | 40 min. | 8 hrs. | 20 hrs. | 2 days |
Physical Properties
| Typical Values | Test Method | ||
|---|---|---|---|
| Compressive strength | 13,500 psi | 945 kg/cm2 | ASTM D-695 |
| Flexural strength | 8,500 psi | 595 kg/cm2 | ASTM D-790 |
| Izod impact strength | 1.3 ft lbs/in | 0.69 j/cm | ASTM D-256 |
| Hardness - Shore D | 86 | ASTM D-2240 | |
| Tensile Shear Adhesion | |||
| Steel | 4000 psi | 280 kg/cm2 | ASTM D-1002 |
| Aluminum | 2800 psi | 196 kg/cm2 | ASTM D-1002 |
| Copper | 2500 psi | 175 kg/cm2 | ASTM D-1002 |
| Stainless Steel | 4100 psi | 287 kg/cm2 | ASTM D-1002 |
| Surface resistivity | 1 x 1015 ohms | ASTM D-257 | |
| Volume resistivity | 1 x 1015 ohm/cm | ASTM D-257 | |
| Dielectric constant | 7.5 | ASTM D-150 | |
| Dielectric strength | 500 volts/mil | ASTM D-115 | |
| Breakdown Voltage | 18.6 Kv | ASTM D-115 | |
Chemical Resistance
| Acetic acid (0-10%) | EX | Methyl alcohol | G |
| Acetic acid (10-20%) | G | Methyl ethyl ketone | G |
| Acetone | G | Nitric acid (0-10%) | EX |
| Aviation fuel | EX | Nitric acid (10-20%) | G |
| Butyl alcohol | EX | Phosphoric acid (0-5%) | EX |
| Calcium chloride | EX | Phosphoric acid (5-10%) | G |
| Crude oil | EX | Potassium chloride | EX |
| Diesel fuel | EX | Propyl alcohol | EX |
| Ethyl alcohol | G | Sodium chloride | EX |
| Gasoline | EX | Sodium hydroxide | EX |
| Heptane | EX | Sulfuric acid (0-10%) | EX |
| Hydrochloric acid (0-10%) | EX | Sulfuric acid (10-20%) | G |
| Hydrochloric acid (10-20%) | G | Toluene | G |
| Kerosene | EX | Xylene | EX |
EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.